- \n
- 30% or better strength to weight ratio over aluminum or steel.<\/li>\n
- 40% lighter than steel, high tensile strength.<\/li>\n
- High corrosion resistance– Titanium pipe is preferred for marine applications because of its excellent resistance to salt water.<\/li>\n
- Low thermal conductivity and expansion.<\/li>\n
- Much greater stiffness than either aluminum or magnesium.<\/li>\n
- Operating temperatures up to 900\u00baF.<\/li>\n
- Self sealing against many corrosives (forms titanium dioxide on its surface).<\/li>\n<\/ul>\n
Cons of Welding with Titanium<\/h2>\n
- \n
- Less stiff and softer than steel.<\/li>\n
- Poor wear properties.<\/li>\n
- Tensile strength decreases with increasing temperature (low creep strength).<\/li>\n
- Flammable in powder form in regular air.<\/li>\n<\/ul>\n
![\"Welding](\"http:\/\/blog.arc-zone.com\/joewelder\/wp-content\/new_ups\/titanium-welding.jpg\" "\\"Welding")
<\/a><\/p>\nWhy Welding With Titanium Can Be A Challenge<\/h2>\n
Many of titanium’s cons directly affect welding, resulting in it getting a reputation as being difficult to work with. At high temperatures, titanium becomes highly reactive to chemicals in its environment. In regular air, welding contaminates titanium with carbides, nitrides, and oxides that make the weld and HAZ (heat-affected zone) brittle, resulting in lower fatigue resistance and notch toughness.<\/p>\n
In addition, chlorine from your sweat or from cleaning compounds can create corrosion on the weld. Thus, the weld and its back side must be protected from contamination to ensure a decent weld. Even friction from grinding wheels (especially aluminum oxide wheels) can develop enough heat and provide the contaminants to undermine the weld.<\/p>\n
Even given these considerations, with careful preparation, any professional welder can obtain quality titanium welds.<\/p>\n
Welding Titanium Tips<\/h2>\n
Because contamination is a primary concern, titanium fabrication demands exacting attention to cleanliness of the metal itself and the shop environment. Often welders working with titanium along with other metals will set an area aside exclusively for titanium fabrication. For acceptable results, that area must be free of air drafts, moisture, dust, grease, and other contaminants and contamination contributors. That means machining, painting, grinding, torch cutting, and the like should not occur in the same area. Ideally, you should minimize humidity to maintain a low dew point.<\/p>\n
Preparing Welding Materials<\/span><\/h3>\n
Perhaps the most important factor in obtaining quality titanium welds is proper preparation and maintenance of the welding materials. The removal of surface contaminants is extremely important. Helpful tips include:<\/p>\n
Material Handling and Storage<\/span><\/p>\n
\u2022 Store parts in a clean, dry area, ensuring they are wrapped and sealed from the environment when not in use. That includes welding wire.<\/p>\n
\u2022 Even clean hands can introduce contamination, so use clean, lint-free gloves when handling materials. Avoid rubber gloves because they may contain chlorine. Instead, use plastic or cotton gloves.<\/p>\n
Material and Surface Preparation<\/span><\/p>\n
\u2022 Joint surfaces must be smooth, clean, and completely free of contamination. Weld joints and wire must be free of mill scale, dirt, dust, grease, oil, moisture, and other contaminants. Any contaminants introduced to the titanium will degrade its performance and corrosion resistance.<\/p>\n
\u2022 When preparing the surface only use a stainless steel brush that is exclusively used on titanium to minimize cross contamination from other metals. After using the brush, rinse it in alcohol and store it in a sealed container.<\/p>\n
\u2022 Use a carbide file to remove any burn marks produced by grinding or mechanical filing. Do not use a steel file, sandpaper, or steel wool, which can leave behind particles in the base metal.<\/p>\n
\u2022 Never use any chlorine-based cleaning solvent.<\/p>\n
\u2022 If you use methyl ethyl ketone (MEK), acetone, or other flammable solvent, be sure that it is completely evaporated prior to striking an arc.<\/p>\n
\u2022 Carefully clean materials prior to welding. Steam cleaning or a dip in a dilute sodium hydroxide solution can remove most of the previously mentioned contaminants. Even so, you will still need to perform a final decontamination to remove any residual contaminants.<\/p>\n
\u2022 Use a hair-dryer-style hot air blower to remove any, perhaps invisible, water condensation immediately before welding. Do not use the blower on flammable solvents.<\/p>\n
\u2022 To speed up the cleaning process, we recommend EZ Wipes, which are lint-free fabric wipes stored in a convenient shop canister. One side of the wipe is mildly abrasive to loosen stuck contaminants, and the other side is smooth for a final go over. The wipes are acetone-free, safe, easy to use, and disposable in regular trash with no special handling.<\/p>\n
\u2022 Clean titanium with light oxide scaling by acid pickling. A common pickling solution is 48% hydro-fluoric acid and 70% nitric acid. Metals to be welded should be pickled for 1 to 20 minutes at a bath temperature from 80 to 160\u00b0F. After pickling, rinse the parts in hot water. With heavier scaling, you may need to precede the pickling by mechanical removal or more radical high-temperature pickling.<\/p>\n
\u2022 If you cannot weld immediately after cleaning, cover the weld joints with paper or plastic to avoid recontamination.<\/p>\n
Grinding<\/span><\/p>\n
\u2022 Use carbide grit wheels for grinding. Avoid aluminum wheels that can introduce contamination.<\/p>\n
\u2022 When grinding, go slow and gentle to keep the titanium\u2019s temperature down. Above 500oF scaling can occur. Remember titanium has low thermal conductivity, so heat will not dissipate as quickly as with other metals.<\/p>\n
Welding<\/span><\/p>\n
Once welding begins, the air itself becomes a contaminant to the molten titanium. Oxygen contamination is an extremely common cause of substandard welds. Not only the weld itself but the HAZ and root side of the weld must be shielded from air when their temperature rises to over 800\u00b0F. Usually, pure argon is the preferred shield gas. Occasionally, you\u2019ll see argon mixed with helium. For some high-performance applications, cryogenic (liquid) argon is used. Here are some welding tips:<\/p>\n
Gas Quality<\/span><\/p>\n
Always buy your gas from a trusted supplier. The argon must be 99.999% pure to ensure the weld isn’t discolored from contamination. That\u2019s 10 parts per million or less contamination. A perfect titanium weld looks like frozen mercury and has little or no coloration. Any blue tinting or mottling often means the argon was not pure enough.<\/p>\n
Leaks and Welding-Related Contaminants<\/span><\/p>\n
\u2022 Make sure all the leads, fittings, and supply hoses have been tested for leaks to ensure there is no oxygen contamination. Be sure to check torch insulators and O-rings for proper fit and seal.<\/p>\n
\u2022 Use a high-quality TIG\/GTAW torch<\/a> to minimize the likelihood of leaks.<\/p>\n
\u2022 Clamps and fixtures near titanium over 750\u00b0F may contaminate the weld.<\/p>\n
Gas Shield<\/span><\/p>\n
\u2022 Probably the biggest difference when welding titanium is the absolute requirement to maintain a shield on the weld\u2019s backside on thinner materials where the back is affected by heat. With complex smaller parts, it is often desirable to use a glove box filled with argon. For larger parts, use special polyethylene purge gas chambers (glove bags)<\/a>. Arc-Zone.com sells a variety of these for many applications, including clamshell models to fit a variety of pipe sizes.<\/p>\n
\u2022 Arc-Zone carries a wide range of purge-gas shielding products, <\/a>including purge baffles, bladders, films, and plugs.<\/p>\n
\u2022 Use an oxygen sensor or monitor to ensure the efficacy of your purge gas shield. Arc-Zone.com offers a variety of models from low-cost, hand-held ones to precision ones that detect oxygen down to one ppm.<\/p>\n
\u2022 Use a quality trailing shield attached to the trailing side of your TIG torch to supply additional shielding and protect the molten weld puddle. Generally, trailing shields require a secondary gas source\u00a0and are often custom-made for a particular torch and application; however off-the-shelf carefully engineered devices produce more consistent results. Arc-Zone sells a complete line of quality trail shields and other devices.\u00a0TIG Torch Materials\u2013 Here is the Difference<\/a>.<\/p>\n
\u2022 Adjust the gas flow rate for optimum coverage and torch cooling without creating turbulence.<\/p>\n
\u2022 Use a 1\u201d (25.4mm) large nozzle with a gas lens or gas flow straightener.<\/p>\n
\u2022 We offer a low-cost, high-quality alternative to trail cups and other purge welding devices called the Gas Saver Kit, which has a Pyrex nozzle 1 1\/8\u201d in diameter<\/a>. It provides the ultimate in gas coverage, perfect for creating an inert atmosphere with improved gas flow to minimize turbulence.<\/p>\n
\u2022 To encourage even coverage, start the argon flowing for several seconds before welding.<\/p>\n
\u2022 The protective argon flow should remain on until the titanium has cooled below 500\u00b0F.<\/p>\n
Discoloration<\/span><\/p>\n
\u2022 Too much argon flow can result in mottled or swirl patterns. Argon is denser than air, so it often flows over the surface much as water does. Where eddies occur in the argon, air can become mixed in resulting in swirl patterns. If the shielding is correct (the argon is dispersed evenly), you should see a uniform color.<\/p>\n
\u2022 Titanium discoloration is not always a problem. It indicates there might be a problem. Discoloration occurs in a sequence: straw, brown, purple, blue, dull salmon pink, and grey (with oxide flakes). Each step is more severe and likely to indicate a contamination problem. Welding codes often limit weld discoloration to straw color. Some allow a little blue discoloration in certain applications. On the welded side, light straw and even brown discoloration can be acceptable.<\/p>\n
\u2022 Some discoloration may occur beyond the HAZ. Depending on the criticalness of the weld, that may be acceptable.<\/p>\n
Tungsten Electrodes<\/span><\/p>\n
\u2022 To ensure a quality weld, your choice of tungsten electrodes is especially important when welding titanium. Always buy your tungsten from a trusted supplier to ensure quality, and grind your tungsten on a dedicated tungsten grinder, away from your clean welding environment.<\/p>\n
\u2022 Thoriated tungsten is often recommended for TIG-welding titanium; however it is radioactive and has raised health concerns. 2% ceriated or 1.5% lanthanated tungsten are good non-radioactive alternatives. The former is an older alternative and is only used for lower amperage DC welding applications. The latter has very similar properties to thoriated tungsten and is actually slightly easier to start and keep stable. In addition, it even lasts a little longer because its tip remains a little cooler. Despite these qualities, some specifications still mandate thoriated tungsten. Therefore, Arc-Zone.com offers it and a full range of electrodes<\/a> to best serve our customers.<\/p>\n
\u2022 Arc-Zone\u00a0recommends the non-radioactive ArcTime brand hybrid tungsten electrode<\/a>, formulated with state-of-the-art alloys to deliver balanced migration and evaporation rates as well as outstanding ignition and\u00a0re-ignition\u00a0properties.<\/p>\n
Here you can download your ultimate guide to<\/span> Welding Titanium<\/span><\/a><\/em><\/span><\/h3>\n
About Arc-Zone.com<\/span><\/h3>\n
Jim Watson<\/span><\/p>\n
Jim is CEO and founder of Arc-Zone.com. He is a master fabricator with years of hands-on experience in his own shop and also as a winning motorcycle racer, car builder, and chief mechanic for a top motorsports team. He also has extensive experience in manufacturing, technical sales, and product development. Before launching Arc-Zone.com, he held leadership positions in some of the most respected companies in the welding industry.<\/p>\n
Arc-Zone<\/span><\/p>\n
Under Jim\u2019s direction, Arc-Zone.com<\/a> has led the industry in product innovation and online sales and service, becoming the world\u2019s leading supplier of high-quality, high-performance welding and metal working tools and accessories.<\/p>\n